COMPATIBLE MODELS :
YAMAHA MT-07 14-15
MATERIAL :
6061-T6 Aluminum Alloy: Silicon 0.4~0.8%, Copper 0.15~0.4%, Magnesium
0.8~1.2%, Chromium 0.404~0.35%, Ultimate Tensile Strength 290 MPa 42000 psi,
Bearing Yield Strength 241 MPa 35000 psi, while thickness is less
than0.25" (6.4mm)Tensile Strength is 8% or more. While thickness is
greater than 0.25" (6.4mm), Tensile Strength is 10%.
SURFACE PROCESSING:
Anodized color treatment: Corrosion
resistant and 60 hours anti-UV endurance (testing under 100eV UV exposure for
60 hours before color start fading, whereas natural UV radiation is around
3~10eV).
FEATURE:
The 6061 Aluminum
has gone through T6
heat treatment and offers
better strength, hardness
and flexibility than average 6061.
The crash pad
is made from
POM
material and offers high tensile strength, effectively absorbing the impact
and dispersing the force during an accident.
|